Hind ERS 219




  • Free flowing and non-shrink system.
  • Resistance to acids and alkalis.
  • Moisture insensitive
  • Useful and helps rapid installation process with high strength.
  • It is used for fixing of bearing plates subjected to heavy load for bridges & piers.


Component A – 2 parts by weight: Component B -1 parts by weight: Component C- 9 parts by weight.


Preparation of Surface 

The area to be treated should be properly cleaned by wire brush or shot blasted.


Mix all the Component-B Polyamide Hardener with Component-A Resin. Add Component C Special Aggregate and again mix well, so as not to entrap air into the product. Mix for 2-3 minutes using a drill and paddle (maximum 200-350 R.P.M.).Only required quantity of material to be mixed for immediate use. The mixed material should be kept undisturbed for 2-3 minutes, so that if any entrapped air is there it escapes from the mix.


Clean all tools & equipment immediately after use with, Xylene, Toluene or suitable solvent.


Aspect Comp.A-Liquid, Comp.B -Liquid, Comp.C-Graded Silica
Density 1800 –1900 kg/m3
Mix Ratio Comp.A : Comp.B : Comp C = 2:1:9 by weight
Working Time 40-45 minutes at 270 C +/- 20 C
Compressive Strength Min 50 N/mm2 in 24 hours at 270 C +/- 20 C

75-80 N/mm2 in 7 days at 270 C +/- 20 C

Bond Strength 1.5-2 N/mm2 in 7 days at 270 C +/- 20 C
Tensile Strength 12.5-14 N/mm2 in 7 days at 270 C +/- 20 C
Flexural Strength 20-25 N/mm2 in 7 days at 270 C +/-  20 C
Chemical Resistance Is not affected by wide range of chemicals, oils etc.
Shrinkage Non-shrink


12 months from the date of manufacture in unopened condition and stored in a cool place under shade.


12 & 18, Kg. Kit or as required.


Hind ERS 219 is non-toxic but ingestion is to be avoided. Any splashes to the skin must be washed with water. If contact with eyes occurs, wash well immediately with water and seek medical advice.

Print Friendly
Reviews (0)


There are no reviews yet.

Be the first to review “Hind ERS 219”

Your email address will not be published. Required fields are marked *