Hind ERS 2115,2118,2120


pdf

Description
MIXING RATIO HIND ERS 2115 HIND ERS 2118 HIND ERS 2120
Component A 100 parts by weight 100 parts by weight 100 parts by weight
Component B 50 parts by weight 50 parts by weight 50 parts by weight
Component C 750 parts by weight 900 parts by weight 1000 parts by weight

PROPERTIES

Aspect Off White Off White Off White
Density (Kg/m3 ) 2025-2050 2150-2100 2200-2250
Compressive Strength N/mm²24 hours at 270 C

7 days at 270 C

Min. 25

Min. 55

Min. 25

Min. 50

Min. 25

Min. 50

Tensile Strength (N/mmin 7 days) 10-20 10-20 10-20
Flexural Strength (N/mm2 in 7 days)    20-30    20-30   20-30
Chemical Resistance Unaffected by a wide range of chemicals, oils etc. for all the three.
Pot Life Approximately 50 minutes at 300 C for all the three.
Shrinkage Non-Shrink

APPLICATION

Surface Preparation

The area to be treated should be properly cleaned. The V-groove cut along the cracks, voids, unsound concrete pockets are filled/repaired with HIND ERS mortar after applying bond coat of a HIND ERS- 21P.

 

Mixing:

Mix all the components – B Polyamide Hardener with Component – A Resin, Add Component –C Special Aggregate and again mix well. Mix for 5-7 minutes using a drill and paddle (maximum 500 R.P.M.) or by manually.

SHELF LIFE

12 months from the date of manufacture in unopened condition and stored in a cool place under shade.

PACKING

18 & 36 Kg Kit or as required

HANDLING PRECAUTION 

Hind ERS 2115/2118/2120 are non-toxic and ingestion is to be avoided. Any splashes to the skin must be washed with water. If contact with eyes occurs, wash well immediately with water and seek medical advice.