Hind Crete Plus WPM (E) is a single component highly flexible, non toxic elastomeric waterproofing coating based on modified acrylic polymer.
Hind Crete Plus WPM (E) is used for surface waterproofing of roofs, toilets, basements, swimming pools, water tanks etc. for providing a water impermeable membrane which is highly flexible and ultra violet resistant.
The surface should be cleaned from all loose materials, oil, grease, and washed properly. Any undulations, pot holes , wide cracks are to be properly mended with cement mortar and sufficiently cured. Before the application of Hind Crete Plus WPM (E) it is to be ensured that there is no stagnant water on the surface.
After the preparation of surface Hind Crete Plus WPM (E) is applied in three coats.
In the 1st coat Hind Crete Plus WPM ( E ) is mixed with clean water in the ratio 1 : 1 ( 1 part Hind Crete Plus WPM (E) : 1 part clean water ) and painted on the prepared surface with a flat paint brush @ 0.500 Kg / Sq. Mtr. of the diluted mixture.
When the 1st coat of diluted Hind Crete Plus WPM ( E ) is touch dry approximately after 4 hours of 1st coat, the 2nd coat of Hind Crete Plus WPM ( E ) is applied without any dilution on the surface with a paint brush @ 0.450 Kg / Sq. Mtr.
After a minimum time interval of 10 hours the third coat of Hind Crete Plus WPM ( E ) is applied without any dilution with a paint brush @ 0.250 Kg /Sq. Mtr.
A final air curing time of 48 hours is sufficient for complete curing of Hind Crete Plus WPM (E) .
0.950 Kg /Sq. Mtr on a smooth surface in three coats for a Dry Film Thickness (DFT) of 0.5-0.6 mm .The coverage depend on the texture and porosity of the surface.
|Solid Content ( % age )||55- 57|
|Tensile Strength (Mpa)||2.8|
|Elongation ( % age )||600 as per ASTM D 412|
|UVTR Resistance 10000 Hrs||No failure as per ASTM D 822|
12 months from the date of manufacture in unopened condition. Should be stored in a cool and dry place away from direct sunlight.
5 Kg, 20 Kg in HDPE Containers
Hind Crete Plus WPM (E) is non toxic, prolonged skin contact should be avoided. In case of contact with eyes occurs wash with plenty of clean water and seek medical advice.
Note: The properties are based on laboratory conditions which may vary at site and in extreme weather conditions.